Nickel Alloy 200 Capillary Tubes Wst. 2.4066 / 2.4068 UNS N02200 / N02201 Nickel 99.2 / LC-nickel 99.2:-

Specification:  ASTM B 161/B 163
EN 10216-5
Maximum expose temperature: 360°C /680°F

Nickel 200 and nickel 201 are solid solution strengthened, commercially pure 99% nickel alloy. Nickel 201 was a modification of 200 to control carbon (0.02% max), this lower carbon content reduces hardness and makes the alloy 201 suitable for cold-formed items and use at higher temperatures. The elemental restrictions of both resulting in a single alloy with the desired characteristics of both alloys, nickel 200/201. Nickel 200 and nickel 201 are combined into one dual-certified chemistry.

Characteristics:

  •     High resistance to various reducing chemicals
  •     Widely used to handle caustic soda
  •     Resistance to numerous organic solutions and caustic lye
  •     Good resistance to neutral and alkaline salt solutions
  •     Resistance to hydrochloric acid and chlorination of hydro carbons as benzene, methane and ethane

Market applications:

  •    Petrochemical industry
  •    Salt production plants 
  •    Floor and chloric processing
  •    Food production
  •    Marine and offshore engineering

Technical details

Technical composition (%) Fe Ni Mn Cu Si C S
200 min - 99.0 - - - - -
max 0.40 - 0.35 0.25 0.35 0.150 0.010
201 min - 99.0 - - - - -
max 0.40 - 0.35 0.25 0.35 0.020 0.010


Mechanical Properties 200 201
Tensile strenght (mpa, min) 380 345
Yield strength (0.2% offset mpa, min) 100 80
Elongation (%, min) 40 40
Density / weight (g / cm3 / kg) 8.89 8.89